ARC BRAZING:A brazing process wherein the heat is obtained from an electric arc formed between the base metal and an electrode, or between two electrodes.

ARC CUTTING: A group of cutting processes in which the cutting of metals is accomplished by melting with the heat of an arc between the electrode and the base metal. See CARBON-ARC CUTTING, METAL-ARC CUTTIING, ARC-OXYGEN CUTTING, AND AIR-ARC CUTTING.

ARC FORCE - Also called Dig and Arc Control. Gives a power source variable additional amperage during low voltage (short arc length) conditions while welding. Helps avoid "sticking" stick electrodes when a short arc length is used.

ARC FAN - The fan-shaped flame associated with the atomic-hydrogen arc.

ARC LENGTH: The distance between the tip of the electrode and the weld puddle.

ARC-OXYGEN CUTTING: An oxygen-cutting process used to sever metals by a chemical reaction of oxygen with a base metal at elevated temperatures.

ARC VOLTAGE: The voltage across the welding arc.

ARC WELDING: A group of welding processes in which fusion is obtained by heating with an electric arc or arcs, with or without the use of filler metal.

AS WELDED: The condition of weld metal, welded joints, and weldments after welding and prior to any subsequent thermal, mechanical, or chemical treatments.

ATOMIC HYDROGEN WELDING: An arc welding process in which fusion is obtained by heating with an arc maintained between two metal electrodes in an atmosphere of hydrogen. Pressure and/or filler metal may or may not be used.

AUSTENITE: The non-magnetic form of iron characterized by a face-centered cubic lattice crystal structure. It is produced by heating steel above the upper critical temperature and has a high solid solubility for carbon and alloying elements.

AUTO-LINK AND REG - Internal inverter power source circuit that automatically links the power source to the primary voltage being applied, without the need for manually linking primary voltage terminals.

AUTOMATIC WELDING - Uses equipment which welds without the constant adjusting of controls by the welder or operator. Equipment controls joint alignment by using an automatic sensing device.

AXIS OF A WELD: A line through the length of a weld, perpendicular to a cross section at its center of gravity.

BUCKLING: Distortion caused by the heat of a welding process.

BUILDUP SEQUENCE: The order in which the weld beads of a multipass weld are deposited with respect to the cross section of a joint. See BLOCK SEQUENCE.

BURN BACK: Fusing of the electrode wire to the current contact tube by sudden lengthening of the arc in any form of automatic or semi-automatic metal-arc welding using a bare electrode.

BURN-OFF RATE : The linear rate of consumption of a consumable electrode

BURN THROUGH : A localised collapse of the molten pool due to (Melt through)

BUTT JOINT: A joint between two workpieces in such a manner that the weld joining the parts is between the surface planes of both of the pieces joined.

BUTT WELD: A weld in a butt joint.

BUTTER WELD: A weld caused of one or more string or weave beads laid down on an unbroken surface to obtain desired properties or dimensions.

CAPILLARY ATTRACTION: The phenomenon by which adhesion between the molten filler metal and the base metals, together with surface tension of the molten filler metal, causes distribution of the filler metal between the properly fitted surfaces of the joint to be brazed.

CARBON ARC WELDING - Arc welding using a carbon electrode or electrodes

CHAIN INTERMITTENT WELD- An intermittent weld on each side of a joint (usually fillet welds in T and lap joints) arranged so that the welds lie opposite to one another along the joint.

CARBIDE PRECIPITATION: A condition occurring in austenitic stainless steel which contains carbon in a supersaturated solid solution. This condition is unstable. Agitation of the steel during welding causes the excess carbon in solution to precipitate. This effect is also called weld decay.

CARBON-ARC CUTTING: A process of cutting metals with the heat of an arc between a carbon electrode and the work.

CARBON-ARC WELDING: A welding process in which fusion is produced by an arc between a carbon electrode and the work. Pressure and/or filler metal and/or shielding may or may not be used.

CARBURIZING FLAME: An oxyacetylene flame in which there is an excess of acetylene. Also called excess acetylene or reducing flame.

CASCADE SEQUENCE: Subsequent beads are stopped short of a previous bead, giving a cascade effect.

CASE HARDENING: A process of surface hardening involving a change in the compsition of the outer layer of an iron base alloy by inward diffusion from a gas or liquid, followed by appropriate thermal treatment. Typical hardening processes are carburizing, cyaniding, carbonitriding, and nitriding.

CHAIN INTERMITTENT FILLET WELDS: Two lines of intermittent fillet welds in a T or lap joint in which the welds in one line are approximately opposite those in the other line.

CHAMFERING: The preparation of a welding contour, other than for a square groove weld, on the edge of a joint member.

CO2 FLUX WELDING - Metal-arc welding in which a flux-coated or flux containing electrode is deposited under a shield of carbon dioxide.

CO2 WELDING - Metal-arc welding in which a bare wire electrode is used the arc and molten pool being shielded with carbon dioxide.

COALESCENCE: The uniting or fusing of metals upon heating.

COATED ELECTRODE: An electrode having a flux applied externally by dipping, spraying, painting, or other similar methods. Upon burning, the coat produces a gas which envelopes the arc.

COMMUTORY CONTROLLED WELDING: The making of a number of spot or projection welds in which several electrodes, in simultaneous contact with the work, progressively function under the control of an electrical commutating device.

COMPOSITE ELECTRODE: A filler metal electrode used in arc welding, consisting of more than one metal component combined mechanically. It may or may not include materials that improve the properties of the weld, or stabilize the arc.

COMPOSITE JOINT: A joint in which both a thermal and mechanical process are used to unite the base metal parts.

CONCAVITY: The maximum perpendicular distance from the face of a concave weld to a line joining the toes.

CONCAVE FILLET WELD : A fillet weld in which the weld face is concave (curved inwards).

CONCURRENT HEATING: Supplemental heat applied to a structure during the course of welding.

CONE: The conical part of a gas flame next to the orifice of the tip.

CONSUMABLE INSERT: Preplaced filler metal which is completely fused into the root of the joint and becomes part of the weld.

CONSTANT CURRENT (CC) WELDING MACHINE : These welding machines have limited maximum short circuit current. They have a negative volt-amp curve and are often referred to as "droopers". The voltage will change with different arc lengths while only slightly varying the amperage, thus the name constant current or variable voltage.

CONSTANT-FEED WIRE FEEDER : Feeder operates from 24 or 115 VAC supplied by the welding power source.

CONSTANT VOLTAGE (CV), CONSTANT POTENTIAL (CP) Welding Machine : "Potential" and "voltage" are basically the same in meaning. This type of welding machine output maintains a relatively stable, consistent voltage regardless of the amperage output. It results in a relatively flat volt-amp curve as opposed to the drooping volt-amp curve of a typical Stick (SMAW) welding machine.

CONVEXITY: The maximum perpendicular distance from the face of a convex fillet weld to a line joining the toes.

CONTINUOUS WELD - A weld extending along the entire length of a joint.

CORNER JOINT: A joint between two members located approximately at right angles to each other in the form of an L.

COUPON PLATE - A test piece made by adding plates to the end of a joint to give an extension of the weld for test purposes. (Note: this term is usually used in the shipbuilding industry.)

COVER GLASS: A clear glass used in goggles, hand shields, and helmets to protect the filter glass from spattering material.

COVERED ELECTRODE: A metal electrode with a covering material which stabilizes the arc and improves the properties of the welding metal. The material may be an external wrapping of paper, asbestos, and other materials or a flux covering.

CRACK: A fracture type discontinuity characterized by a sharp tip and high ratio of length and width to opening displacement.

CRATER: A depression at the termination of an arc weld.

CRITICAL TEMPERATURE: The transition temperature of a substance fromm one crystalline form to another.

CURRENT - Another name for amperage. The amount of electricity flowing past a point in a conductor every second.

CURRENT DENSITY: Amperes per square inch of the electrode cross sectional area.

CUTTING ELECTRODE - An electrode with a covering that aids the production of such an arc that molten metal is blown away to produce a groove or cut in the work.

CUTTING OXYGEN - Oxygen used at a pressure suitable for cutting.

CUTTING TIP: A gas torch tip especially adapted for cutting.

CUTTING TORCH: A device used in gas cutting for controlling the gases used for preheating and the oxygen used for cutting the metal

CYLINDER: A portable cylindrical container used for the storage of a compressed gas.

Direct Current Electrode Negative (DCEN)-The specific direction of current flow through a welding circuit when the electrode lead is connected to the negative terminal and the work lead is connected to the positive terminal of a DC welding machine. Also called direct current, straight polarity (DCSP).

Direct Current Electrode Positive (DCEP)- The specific direction of current flow through a welding circuit when the electrode lead is connected to a positive terminal and the work lead is connected to a negative terminal to a DC welding machine. Also called direct current, reverse polarity (DCRP).

Drag - The projected distance between the two ends of a drag line.

Duty Cycle-The number of minutes out of a 10-minute time period an arc welding machine can be operated at maximum rated output. An example would be 60% duty cycle at 300 amps. This would mean that at 300 amps the welding machine can be used for 6 minutes and then must be allowed to cool with the fan motor running for 4 minutes. (Some manufacturers rate machines on a 5 minute cycle).

DEFECT: A discontinuity or discontinuities which, by nature or accumulated effect (for example, total crack length), render a part or product unable ot meet the minimum applicable acceptance standards or specifications. This term designates rejectability.

DEPOSITED METAL: Filler metal that has been added during a welding operation.

DEPOSITION EFFICIENCY: The ratio of the weight of deposited metal to the net weight of electrodes consumed, exclusive of stubs.

DEPTH OF FUSION: The distance from the original surface of the base metal to that point at which fusion ceases in a welding operation.

DE-SEAMING - A method of metal-arc welding in which fused particles of the electrode wire in contact with the molten pool are detached from the electrode in rapid succession by the short circuit current, which develops every time the wire touches the molten pool.

DIE: a. Resistance Welding. A member, usually shaped to the work contour, used to clamp the parts being welded and conduct the welding current. b. Forge Welding. A device used in forge welding primarily to form the work while hot and apply the necessary pressure.

DIE WELDING: A forge welding process in which fusion is produced by heating in a furnace and by applying pressure by means of dies.

DIP BRAZING: A brazing process in which bonding is produced by heating in a molten chemical or metal bath and by using a nonferrous filler metal having a melting point above 800 °F (427 °C), but below that of the base metals. The filler metal is distributed in the joint by capillary attraction. When a metal bath is used, the bath provides the filler metal.

DIRECT CURRENT ELECTRODE NEGATIVE (DCEN): The arrangement of direct current arc welding leads in which the work is the positive pole and the electrode is the negative pole of the welding arc.

DIRECT CURRENT ELECTRODE POSITIVE (DCEP): The arrangenwmt of direct current arc welding leads in which the work is the negative pole and the electrode is the positive pole of the welding arc.

DISCONTINUITY: An interruption of the typical structure of a weldment, such as lack of homogeneity in the mechanical, metallurgical, or physical characteristics of the material or weldment. A discontinuity is not necessarily a defect.

DRAG: The horizontal distance between the point of entrance and the point of exit of a cutting oxygen stream.

DUCTILITY: The property of a metal which allows it to be permanently deformed, in tension, before final rupture. Ductility is commonly evaluated by tensile testing in which the amunt of elongation and the reduction of area of the broken specimen, as compared to the original test specimen, are measured and calculated.

DUTY CYCLE: The percentage of time during an arbitrary test period, usually 10 minutes, during which a power supply can be operated at its rated output without overloading.

EDGE JOINT: A joint between the edges of two or more parallel or nearly parallel members.

EDGE PREPARATION: The contour prepared on the edge of a joint member for welding

EFFECTIVE LENGTH OF WELD: The length of weld throughout which the correctly proportined cross section exits.

ELECTRODE: a. Metal-Arc. Filler metal in the form of a wire or rod, whether bare or covered, through which current is conducted between the electrode holder and the arc. b. Carbon-Arc. A carbon or graphite rod through which current is conducted between the electrode holder and the arc. c.Atomic Hydroqen. One of the two tungsten rods between the points of which the arc is maintained. d. Electrolytic Oxygen-Hydrogen Generation. The conductors by which current enters and leaves the water, which is decomposed by the passage of the current. e. Resistance Welding. The part or parts of a resistance welding machine through which the welding current and the pressure are applied directly to the work.

ELECTRODE FORCE: a. Dynamic. In spot, seam, and projection welding, the force (pounds) between the electrodes during the actual welding cycle. b. Theoretical. In spot, seam, and projection welding, the force, neglecting friction and inertia, available at the electrodes of a resistance welding machine by virtue of the initial force application and the theoretical mechanical advantage of the system. c. Static. In spot, seam, and projection welding, the force between the electrodes under welding conditions, but with no current flowing and no movement in the welding machine.

ELECTRODE HOLDER: A device used for mechanically holding the electrode and conduct- ing current to it.

ELECTRODE SKID: The sliding of an electrode along the surface of the work during spot, seam, or projection welding.

ELECTRON-BEAM CUTTING: Thermal cutting in vacuum by melting and vaporising a narrow section of the metal by the impact of a focused beam of electrons.

EMBOSSMENT: A rise or protrusion frcm the surface of a metal.

ETCHING: A process of preparing metallic specimens and welds for macrographic or micrographic examination.

Excess penetration bead - Excessive metal protruding through the root of a fusion weld made from one side only.

FAYING SURFACE: That surface of a member that is in contact with another member to which it is joined.

FEATHER : The carbon-rich zone, visible in a flame, extending around and beyond the cone when there is an excess of carbonaceous gas.

FERRITE: The virtually pure form of iron existing below the lower critical temperature and characterized by a body-centered cubic lattice crystal structure. It is magnetic and has very slight solid solubility for carbon.

FILLER METAL: Metal to be added in making a weld.

FILLET WELD: A weld of approximately triangular cross section, as used in a lap joint, joining two surfaces at approximately right angles to each other.

FILTER GLASS: A colored glass used in goggles, helmets, and shields to exclude harmful light rays.

FIXED AUTOMATION : Automated, electronically controlled welding system for simple, straight or circular welds.

FLAME CUTTING: see OXYGEN CUTTING.

FLAME GOUGING: See OXYGEN GOUGING.

FLAME HARDENING: A method for hardening a steel surface by heating with a gas flame followed by a rapid quench.

FLAME SOFTENING: A method for softening steel by heating with a gas flame followed by slow cooling.

FLASH: Metal and oxide expelled from a joint made by a resistance welding process.

FLASH WELDING: A resistance welding process in which fusion is produced, simultaneously over the entire area of abutting surfaces, by the heat obtained from resistance to the flow of current between two surfaces and by the application of pressure after heating is substantially completed. Flashing is accompanied by expulsion of metal from the joint.

FLASHBACK: The burning of gases within the torch or beyond the torch in the hose, usually with a shrill, hissing sound.

FLAT POSITION: The position in which welding is performed from the upper side of the joint and the face of the weld is approximately horizontal.

FLEXIBLE AUTOMATION : Automated, robotically controlled welding system for complex shapes and applications where welding paths require torch-angle manipulation.

FILM BRAZING: A process in which bonding is produced by heating with a molten nonferrous filler metal poured over the joint until the brazing temperature is attained. The filler metal is distributed in the joint by capillary attraction. See BRAZING.

FLOW WELDING: A process in which fusion is produced by heating with molten filler metal poured over the surfaces to be welded until the welding temperature is attained and the required filler metal has been added. The filler metal is not distributed in the joint by capillary attraction.

FLUX: A cleaning agent used to dissolve oxides, release trapped gases and slag, and to cleanse metals for welding, soldering, and brazing.

FLUX CORED ARC WELDING (FCAW) : An arc welding process which melts and joins metals by heating them with an arc between a continuous, consumable electrode wire and the work. Shielding is obtained from a flux contained within the electrode core. Depending upon the type of flux-cored wire, added shielding may or may not be provided from externally supplied gas or gas mixture. Consumables: contact tips, flux cored wire, shielding gas (if required, depends on wire type).

FOREHAND WELDING: A gas welding technique in which the flare is directed against the base metal ahead of the completed weld.

FORGE WELDING: A group of welding processes in which fusion is produced by heating in a forge or furnace and applying pressure or blows.

FREE BEND TEST: A method of testing weld specimens without the use of a guide.

FULL FILLET WELD: A fillet weld whose size is equal to the thickness of the thinner member joined.

FURNACE BRAZING: A process in which bonding is produced by the furnace heat and a nonferrous filler metal having a melting point above 800 °F (427 °C), but below that of the base metals. The filler metal is distributed in the joint by capillary attraction.

FUSION: A thorough and complete mixing between the two edges of the base metal to be joined or between the base metal and the filler metal added during welding.

FUSION ZONE (FILLER PENETRATION): The area of base metal melted as determined on the cross section of a weld.

GAS METAL-ARC (MIG) WELDING (GMAW): An arc welding process in which fusion is produced by heating with an electric arc between a metal electrode and the work. Shielding is obtained from an inert gas such as helium or argon. Pressure and/or filler metal may or my not be used.

GAS POCKET: A weld cavity caused by the trapping of gases releasd by the metal when cooling.

GAS TUNGSTEN-ARC (TIG) WELDING (GTAW): An arc welding process in which fusion is produced by heating with an electric arc between a tungsten electrode and the work while an inert gas forms around the weld area to prevent oxidation. No flux is used.

GAS WELDING: A process in which the welding heat is obtained from a gas flame.

GLOBULAR TRANSFER (ARC WELDING): A type of metal transfer in which molten filler metal is transferred across the arc in large droplets.

GOGGLES: A device with colored lenses which protect the eyes from harmful radiation during welding and cutting operations.

GROOVE: The opening provided between two members to be joined by a groove weld.

GROOVE ANGLE: The total included angle of the groove between parts to be joined by a groove weld.

GROOVE FACE: That surface of a member included in the groove.

GROOVE RADIUS: The radius of a J or U groove.

GROOVE WELD: A weld made by depositing filler metal in a groove between two members to be joined.

GROUND CONNECTION: The connection of the work lead to the work.

GROUND LEAD: See WORK LEAD.

GUIDED BEND TEST: A bending test in which the test specimen is bent to a definite shape by means of a jig.

HAND SHIELD: A device used in arc welding to protect the face and neck. It is equipped with a filter glass lens and is designed to be held by hand.

HARD FACING: A particular form of surfacing in which a coating or cladding is applied to a surface for the main purpose of reducing wear or loss of material by abrasion, impact, erosion, galling, and cavitation.

HARD SURFACING: The application of a hard, wear-resistant alloy to the surface of a softer metal.

HARDENING: a. The heating and quenching of certain iron-base alloys from a temperature above the critical temperature range for the purpose of producing a hardness superior to that obtained when the alloy is not quenched. This term is usually restricted to the formtion of martensite. b. Any process of increasing the hardness of metal by suitable treatment, usually involving heating and cooling.

HEAT AFFECTED ZONE: That portion of the base metal whose structure or properties have been changed by the heat of welding or cutting.

HEAT TIME: The duration of each current impulse in pulse welding.

HEAT TREATMENT: An operation or combination of operations involving the heating and cooling of a metal or an alloy in the solid state for the purpose of obtaining certain desirable conditions or properties. Heating and cooling for the sole purpose of mechanical working are excluded frcm the meaning of the definition.

HEATING GATE: The opening in a thermit mold through which the parts to be welded are preheated.

HELMET: A device used in arc welding to protect the face and neck. It is equipped with a filter glass and is designed to be worn on the head.

HERTZ : Hertz is often referred to as "cycles per second". In the United States, the frequency or directional change of alternating current is usually 60 hertz.

HIGH FREQUENCY : Covers the entire frequency spectrum above 50,000 Hz. Used in TIG welding for arc ignition and stabilization.

HOLD TIME: The time that pressure is maintained at the electrodes after the welding current has stopped.

HORIZONTAL WELD: A bead or butt welding process with its linear direction horizontal or inclined at an angle less than 45 degrees to the horizontal, and the parts welded being vertically or approximately vertically disposed.

HORN: The electrode holding arm of a resistance spot welding machine.

HORN SPACING: In a resistance welding machine, the unobstructed work clearance between horns or platens at right angles to the throat depth. This distance is measured with the horns parallel and horizontal at the end of the downstroke.

HOT SHORT: A condition which occurs when a metal is heated to that point, prior to melting, where all strength is lost but the shape is still maintained.

HOTSTART^TM : Used on some Stick (SMAW) machines to make it easier to start difficult-to-start electrodes. Used for arc starting only.

HYDROGEN BRAZING: A method of furnace brazing in a hydrogen atmosphere.

HYDROMATIC WELDING: See PRESSURE CONTROLLED WELDING.

HYGROSCOPIC: Readily absorbing and retaining moisture.

IMPREGNATED-TAPE METAL-ARC WELDING An arc welding process in which fusion is produced by heating with an electric arc between a metal electrode and the work. Shielding is obtained from decomposition of impregnated tape wrapped around the electrode as it is fed to the arc. Pressure is not used, and filler metal is obtained from the electrode.

INDUCTION BRAZTNG: A process in which bonding is produced by the heat obtained from the resistance of the work to the flow of induced electric current and by using a nonferrous filler metal having a melting point above 800 °F (427 °C), but below that of the base metals. The filler metal is distributed in the joint by capillary attraction.

INDUCTION WELDING: A process in which fusion is produced by heat obtained from resistance of the work to the flow of induced electric current, with or without the application of pressure.

INERT GAS: A gas which does not normally combine chemically with the base metal or filler metal.

INTERPASS TEMPERATURE: In a multipass weld, the lowest temperature of the deposited weld meal before the next pass is started.

INVERTER : Power source which increases the frequency of the incoming primary power, thus providing for a smaller size machine and improved electrical characteristics for welding, such as faster response time and more control for pulse welding.

JOINT PENETRATION: The maximum depth a groove weld extends from its face into a joint, exclusive of reinforcement.

KW : Kilowatts. Primary KW is the actual power used by the power source when it is producing its rated output. Secondary KW is the actual power output of the welding power source. Kilowatts are found by taking volts times amps divided by 1,000 and taking into account any power factor.

LAYER: A stratum of weld metal, consisting of one or more weld beads.

LEG OF A FILLET WELD: The distance from the root of the joint to the toe of the fillet weld.

LIFT-ARC^TM : This feature allows TIG arc starting without high frequency. Starts the arc at any amperage without contaminating the weld with tungsten.

LIQUIDUS: The lowest temperature at which a metal or an alloy is completely liquid.

LOCAL PREHEATNG: Preheating a specific portion of a structure.

LOCAL STRESS RELIEVING: Stress relieving heat treatment of a specific portion of a structure.

MARTENSITE: Martensite is a microconstituent or structure in quenched steel characterized by an acicular or needle-like pattern on the surface of polish. It has the maximum hardness of any of the structures resulting from the decomposition products of austenite.

MASH SEAM WELDING: A seam weld made in a lap joint in which the thickness at the lap is reduced to approximately the thickness of one of the lapped joints by applying pressure while the metal is in a plastic state.

MELTING POINT: The temperature at which a metal begins to liquefy.

MELTING RANGE: The temperature range between solidus and liquidus.

MELTING RATE: The weight or length of electrode melted in a unit of time.

METAL-ARC CUTTING: The process of cutting metals by melting with the heat of the metal arc.

METAL-ARC WELDING: An arc welding process in which a metal electrode is held so that the heat of the arc fuses both the electrode and the work to form a weld.

METALLIZING: A method of overlay or metal bonding to repair worn parts.

MICROPROCESSOR - One or more integrated circuits that can be programmed with stored instructions to perform a variety of functions.

MIG (GMAW or Gas Metal Arc Welding)-An arc welding process which joins metals by heating them with an arc. The arc is between a continuously fed filler metal (consumable) electrode and the workpiece. Externally supplied gas or gas mixtures provide shielding. Common MIG welding is also referred to as short circuit transfer. Metal is deposited only when the wire actually touches the work. No metal is transferred across the arc. Another method of MIG welding, spray transfer moves a stream of tiny molten droplets across the arc from the electrode to the weld puddle. Consumables: contact tips, shielding gas, welding wire

MIXING CHAMBER: That part of a welding or cutting torch in which the gases are mixed for combustion.

MULTI-IMPULSE WELDING: The making of spot, projection, and upset welds by more than one impulse of current. When alternating current is used each impulse may consist of a fraction of a cycle or a number of cycles.

NICK BREAK TEST: A method for testing the soundness of welds by nicking each end of the weld, then giving the test specimen a sharp hammer blow to break the weld from nick to nick. Visual inspection will show any weld defects.

NONFERROUS: Metals which contain no iron. Aluminum, brass, bronze, copper, lead, nickel, and titanium are nonferrous.

NORMALIZING: Heating iron-base alloys to approximately 100 °F (38 °C) above the critical temperature range followed by cooling to below that range in still air at ordinary temperature.

NUGGET: The fused metal zone of a resistance weld.

OVERHEAD POSITION: The position in which welding is performed from the underside of a joint and the face of the weld is approximately horizontal.

OVERLAP: The protrusion of weld metal beyond the bond at the toe of the weld.

OXIDIZING FLAME: An oxyacetylene flame in which there is an excess of oxygen. The unburned excess tends to oxidize the weld metal.

OXYACETYLENE CUTTING: An oxygen cutting process in which the necessary cutting temperature is maintained by flames obtained frcm the combustion of acetylene with oxygen.

OXYACETYLENE WELDING: A welding process in which the required temperature is attained by flames obtained from the combustion of acetylene with oxygen.

OXY-ARC CUTTING: An oxygen cutting process in which the necessary cutting temperature is maintained by means of an arc between an electrode and the base metal.

OXY-CITY GAS CUTTING: An oxygen cutting process in which the necessary cutting temperature is maintained by flames obtained from the combustion of city gas with oxygen.

OXYGEN CUTTING: A process of cutting ferrous metals by means of the chemical action of oxygen on elements in the base metal at elevated temperatures.

OXYGEN GOUGING: An application of oxygen cutting in which a chamfer or groove is formed.

OXY-HYDROGEN CUTTING: An oxygen cuting process in which the necessary cutting temperature is maintained by flames obtained from the combustion of city gas with oxygen.

OXY-HYDROGEN WELDING: A gas welding process in which the required welding temperature is attained by flames obtained from the combustion of hydrogen with oxygen.

OXY-NATURAL GAS CUTTING: An oxygen cutting process in which the necessary cutting temperature is maintained by flames obtained by the combustion of natural gas with oxygen.

OXY-PROPANE CUTTING: An oxygen cutting process in which the necessary cutting temperature is maintained by flames obtained from the combustion of propane with oxygen.

PEENING: The mechanical working of metals by means of hammer blows. Peening tends to stretch the surface of the cold metal, thereby relieving contraction stresses.

PENETRANT INSPECTION: a. Fluorescent. A water washable penetrant with high fluorescence and low surface tension. It is drawn into small surface openings by capillary action. When exposed to black light, the dye will fluoresce. b. Dye. A process which involves the use of three noncorrosive liquids. First, the surface cleaner solution is used. Then the penetrant is applied and allowed to stand at least 5 minutes. After standing, the penetrant is removed with the leaner solution and the developer is applied. The dye penetrant, which has remained in the surface discontinuity, will be drawn to the surface by the developer resulting in bright red indications.

PERCUSSIVE WELDING: A resistance welding process in which a discharge of electrical energy and the application of high pressure occurs simultaneously, or with the electrical discharge occurring slightly before the application of pressure.

PERLITE: Perlite is the lamellar aggregate of ferrite and iron carbide resulting from the direct transformation of austenite at the lower critical point.

PITCH: Center to center spacing of welds.

PLASMA ARC CUTTING : An arc cutting process which severs metal by using a constricted arc to melt a small area of the work. This process can cut all metals that conduct electricity. Miller Spectrum cutters are complete packages that contain all required equipment and torch consumables. Consumables: torch consumables, gas or compressed air supply.

PLUG WELD: A weld is made in a hole in one member of a lap joint, joining that member to that portion of the surface of the other member which is exposed through the hole. The walls of the hole may or may not be parallel, and the hole may be partially or completely filled with the weld metal.

POKE WELDING: A spot weldimg process in which pressure is applied manually to one electrode. The other electrode is clamped to any part of the metal much in the same manner that arc welding is grounded.

POROSITY: The presence of gas pockets or inclusions in welding.

POSITIONS OF WELDING: All welding is accomplished in one of four positions: flat, horizontal, overhead, and vertical. The limiting angles of the various positions depend somewhat as to whether the weld is a fillet or groove weld.

POSTHEATING: The appplication of heat to an assembly after a welding, brazing, soldering, thermal spraying, or cutting operation.

POSTWELD INTERVAL: In resistance welding, the heat time between the end of weld time, or weld interval, and the start of hold time. During this interval, the weld is subjected to mechanical and heat treatment.

POUNDS PER SQUARE INCH (psi) - A measurement equal to a mass or weight applied to one square inch of surface area.

POWER EFFICIENCY : How well an electrical machine uses the incoming electrical power.

POWER FACTOR CORRECTION : Normally used on single-phase, constant current power sources, to reduce the amount of primary amperage demanded from the power company while welding.

PREHEATING: The application of heat to a base metal prior to a welding or cutting operation.

PRESSURE CONTROLLED WELDING: The making of a number of spot or projection welds in which several electrodes function progressively under the control of a pressure sequencing device.

PRESSURE WELDING: Any welding process or method in which pressure is used to complete the weld.

PREWELD INTERVAL: In spot, projection, and upset welding, the time between the end of squeeze time and the start of weld time or weld interval during which the material is preheated. In flash welding, it is the time during which the material is preheated.

PRIMARY POWER : Often referred to as the input line voltage and amperage available to the welding machine from the shop's main power line. Often expressed in watts or kilowatts (KW), primary input power is AC and may be single-phase or three-phase. Welding machines with the capability of accepting more than one primary input voltage and amperage must be properly connected for the incoming primary power being used.

PROCEDURE QUALIFICATION: The demonstration that welds made by a specific procedure can meet prescribed standards.

PROJECTION WELDING: A resistance welding process between two or more surfaces or between the ends of one member and the surface of another. The welds are localized at predetermined points or projections.

PULSATION WELDING: A spot, projection, or seam welding process in which the welding current is interrupted one or more times without the release of pressure or change of location of electrodes.

PULSED MIG (MIG-P) : A modified spray transfer process that produces no spatter because the wire does not touch the weld puddle. Applications best suited for pulsed MIG are those currently using the short circuit transfer method for welding steel, 14 gauge (1.8 mm) and up. Consumables: contact tips, shielding gas, welding wire.

PULSED TIG (TIG-P) : A modified TIG process appropriate for welding thinner materials. Consumables: tungsten electrode, filler material, shielding gas.

PULSING : Sequencing and controlling the amount of current, the polarity, and the duration of the welding arc.

PUSH WELDING: The making of a spot or projection weld in which the force is aping current is interrupted one or more times without the release of pressure or change of location of electrodes.

PUSH WELDING: The making of a spot or projection weld in which the force is applied manually to one electrode and the work or a backing bar takes the place of the other electrode.

REACTION STRESS: The residual stress which could not otherwise exist if the members or parts being welded were isolated as free bodies without connection to other parts of the structure.

REDUCING FLAME: See CARBURIZING FLAME.

REGULATOR: A device used to reduce cylinder pressure to a suitable torch working pressure.

REINFORCED WELD: The weld metal built up above the surface of the two abutting sheets or plates in excess of that required for the size of the weld specified.

RESIDUAL STRESS: Stress remaining in a structure or member as a result of thermal and/or mechanical treatment.

RESISITANCE BRAZING: A brazing process in which bonding is produced by the heat obtained from resistance to the flow of electric current in a circuit of which the workpiece is a part, and by using a nonferrous filler metal having a melting point above 800 °F (427 °C), but below that of the base metals. The filler metal is distributed in the joint by capillary attraction.

RESISTANCE BUTT WELDING: A group of resistance welding processes in which the weld occurs simultaneously over the entire contact area of the parts being joined.

RESISTANCE SPOT WELDING (RSW ) : A process in which two pieces of metal are joined by passing current between electrodes positioned on opposite sides of the pieces to be welded. There is no arc with this process, and it is the resistance of the metal to the current flow that causes the fusion. Spot welding requires the following equipment: air- or water-cooled spot welder, set of 2 tongs and set of 2 tips. Consumables are not required to spot weld.

RESISTANCE WELDING: A group of welding processes in which fusion is produced by heat obtained from resistance to the flow of electric current in a circuit of which the workpiece is a part and by the application of pressure.

REVERSE POLARITY: The arrangement of direct current arc welding leads in which the work is the negative pole and the electrode is the positive pole of the welding arc.

RMS : Root Mean Square. The "effective" values of measured AC voltage or amperage. RMS equals 0.707 times the maximum, or peak value.

ROCKWELL HARDNESS TEST: In this test a machine measures hardness by determining the depth of penetration of a penetrator into the specimen under certain arbitrary fixed conditions of test. The penetrator may be either a steel ball or a diamond spherocone.

ROOT: See ROOT OF JOINT and ROOT OF WELD.

ROOT CRACK: A crack in the weld or base metal which occurs at the root of a weld.

ROOT EDGE: The edge of a part to be welded which is adjacent to the root.

ROOT FACE: The portion of the prepared edge of a member to be joined by a groove weld which is not beveled or grooved.

ROOT OF JOINT: That portion of a joint to be welded where the members approach closest to each other. In cross section, the root of a joint may be a point, a line, or an area.

ROOT OF WELD: The points, as shown in cross section, at which the bottom of the weld intersects the base metal surfaces.

ROOT OPENING: The separation between the members to be joined at the root of the joint.

ROOT PENETRATION: The depth a groove weld extends into the root of a joint measured on the centerline of the root cross section.

SCARFING: A process for removing defects and checks which develop in the rolling of steel billets by the use of a low velocity oxygen deseaming torch.

SEAL WELD: A weld used primarily to obtain tightness and to prevent leakage.

SEAM WELDING: Welding a lengthwise seam in sheet metal either by abutting or overlapping joints.

SELECTIVE BLOCK SEQUENCE: A block sequence in which successive blocks are completed in a certain order selected to create a predetermined stress pattern.

SEMIAUTOMATIC WELDING : The equipment controls only the electrode wire feeding. The welding gun movement is controlled by hand.

SERIES WELDING: A resistance welding process in which two or more welds are made simultaneously by a single welding transformer with the total current passing through each weld.

SHEET SEPARATION: In spot, seam, and projection welding, the gap surrounding the weld between faying surfaces, after the joint has been welded.

SHIELDING GAS : Protective gas used to prevent atmospheric contamination of the weld pool.

SHIELDED WELDING: An arc welding process in which protection from the atmosphere is obtained through use of a flux, decomposition of the electrode covering, or an inert gas.

SHOULDER: See ROOT FACE.

SHRINKAGE STRESS: See RESIDUAL STRESS.

SINGLE IMPULSE WELDING: The making of spot, projection, and upset welds by a single impulse of current. When alternating current is used, an impulse may consist of a fraction of a cycle or a number of cycles.

SINGLE-PHASE CIRCUIT : An electrical circuit producing only one alternating cycle within a 360 degree time span.

SIZE OF WELD: a. Groove weld. The joint penetration (depth of chamfering plus the root penetrtion when specified). b. Equal leg fillet welds. The leg length of the largest isosceles right triangle which can be inscribed within the fillet weld cross section. c. Unequal leg fillet welds. The leg length of the largest right triangle which can be inscribed within the fillet weld cross section. d. Flange weld. The weld metal thickness measured at the root of the weld.

SKIP SEQUENCE: See WANDERING SEQUENCE.

SLAG INCLUSION: Non-metallic solid material entrapped in the weld metal or between the weld metal and the base metal.

SLOT WELD: A weld made in an elongated hole in one member of a lap or tee joint joining that member to that portion of the surface of the other member which is exposed through the hole. The hole may be open at one end and may be partially or completely filled with weld metal. (A fillet welded slot should not be construed as conforming to this definition.)

SLUGGING: Adding a separate piece or pieces of material in a joint before or during welding with a resultant welded joint that does not comply with design drawing or specification requirements.

SOLDERING: A group of welding processes which produce coalescence of materials by heating them to suitable temperature and by using a filler metal having a liquidus not exceeding 450 °C (842 °F) and below the solidus of the base materials. The filler metal is distributed between the closely fitted surfaces of the joint by capillary action.

SOLIDUS: The highest temperature at which a metal or alloy is completely solid.

SPACER STRIP: A metal strip or bar inserted in the root of a joint prepared for a groove weld to serve as a backing and to maintain the root opening during welding.

SPALL: Small chips or fragments which are sometimes given off by electrodes during the welding operation. This problem is especially common with heavy coated electrodes.

SPATTER: The metal particles expelled during arc and gas welding which do not form a part of the weld.

SPOT WELDING: A resistance welding process in which fusion is produced by the heat obtained from the resistance to the flow of electric current through the workpieces held together under pressure by electrodes. The size and shape of the individually formed welds are limited by the size and contour of the electrodes.

SPRAY TRANSFER: A type of metal transfer in which molten filler metal is propelled axially across the arc in small droplets.

SQUAREWAVE^TM :The AC output of a power source that has the ability to rapidly switch between the positive and negative half cycles of alternating current.

STAGGERED INTERMITTENT FILLET WELD: Two lines of intermittent welding on a joint, such as a tee joint, wherein the fillet increments in one line are staggered with respect to those in the other line.

STICK WELDING (SMAW or Shielded Metal Arc) :An arc welding process which melts and joins metals by heating them with an arc, between a covered metal electrode and the work. Shielding gas is obtained from the electrode outer coating, often called flux. Filler metal is primarily obtained from the electrode core. An AC/DC welder is recommended for Stick. For most applications, DC reverse polarity welding offers advantages over AC, including easier starts and out-of-position welding, smoother arc and fewer arc outages and sticking. Consumables: stick electrodes.

STORED ENERGY WELDING: The making of a weld with electrical energy accumulated electrostatically, electronagnetically, or electrochemically at a relatively low rate and made available at the required welding rate.

STRAIGHT POLARITY: The arrangement of direct current arc welding leads in which the work is the positive pole and the electrode is the negative pole of the welding arc.

STRESS RELIEVING: A process of reducing internal residual stresses in a metal object by heating to a suitable temperature and holding for a proper time at that temperature. This treatment may he applied to relieve stresses induced by casting, quenching, normalizfig, machining, cold working, or welding.

STRING BEAD WELDING: A method of metal arc welding on pieces 3/4 in. (19 mm) thick or heavier in which the weld metal is deposited in layers composed of strings of beads applied directly to the face of the bevel.

STUD WELDING: An arc welding process in which fusion is produced by heating with an electric arc drawn between a metal stud, or similar part, and the other workpiece, until the surfaces to be joined are properly heated. They are brought together under pressure.

SUBMERGED ARC WELDING: An arc welding process in which fusion is produced by heating with an electric arc or arcs between a bare metal electrode or electrodes and the work. The welding is shieldd by a blanket of granular, fusible material on the work. Pressure is not used. Filler metal is obtained from the electrode, and sometimes from a supplementary welding rod.

SURFACING: The deposition of filler metal on a metal surface to obtain desired properties or dimensions.

TEE JOINT : A joint between two members located approximately at right angles to each other in the form of a T.

TEMPER COLORS: The colors which appear on the surface of steel heated at low temperature in an oxidizing atmosphere.

TEMPER TIME: In resistance welding, that part of the postweld interval during which a current suitable for tempering or heat treatment flows. The current can be single or multiple impulse, with varying heat and cool intervals.

TEMPERING: Reheating hardened steel to some temperature below the lower critical temperature, followed by a desired rate of cooling. The object of tempering a steel that has been hardened by quenching is to release stresses set up, to restore some of its ductility, and to develop toughness through the regulation or readjustment of the embrittled structural constituents of the metal. The temperature conditions for tempering may be selected for a given composition of steel to obtain almost any desired combination of properties.

TENSILE STRENGTH: The maximum load per unit of original cross-sectional area sustained by a material during the tension test.

TENSION TEST: A test in which a specimen is broken by applying an increasing load to the two ends. During the test, the elastic properties and the ultimate tensile strength of the material are determined. After rupture, the broken specimen may be measured for elongation and reduction of area.

THERMIT CRUCIBLE The vessel in which the thermit reaction takes place.

THERMIT MIXTURE: A mixture of metal oxide and finely divided aluminum with the addition of alloying metals as required.

THERMIT MOLD: A mold formed around the parts to be welded to receive the molten metal.

THERMIT REACTION: The chemical reaction between metal oxide and aluminum which produces superheated molten metal and aluminum oxide slag.

THERMIT WELDING: A group of welding processes in which fusion is produced by heating with superheated liquid metal and slag resulting from a chemical reaction between a metal oxide and aluminum, with or without the application of pressure. Filler metal, when used, is obtained from the liquid metal.

THROAT DEPTH: In a resistance welding machine, the distance from the centerline of the electrodes or platens to the nearest point of interference for flatwork or sheets. In a seam welding machine with a universal head, the throat depth is measured with the machine arranged for transverse welding.

THROAT OF FILLET WELD: a. Theoretical. The distance from the beginning of the root of the joint perpendicular to the hypotenuse of the largest right triangle that can be inscribed within the fillet-weld cross section. b. Actual. The distance from the root of the fillet weld to the center of its face.

TIG WELDING (GTAW or Gas Tungsten Arc) : Often called TIG welding (Tungsten Inert Gas), this welding process joins metals by heating them with a tungsten electrode which should not become part of the completed weld. Filler metal is sometimes used and argon inert gas or inert gas mixtures are used for shielding. Consumables: tungsten electrode, filler metal, shielding gas.

THREE-PHASE CIRCUIT : An electrical circuit delivering three cycles within a 360 degree time span, and the cycles are 120 electrical degrees apart.

TOE CRACK: A crack in the base metal occurring at the toe of the weld.

TOE OF THE WELD: The junction between the face of the weld and the base metal.

TORCH: See CUTTING TORCH or WELDING TORCH.

TORCH BRAZING: A brazing process in which bonding is produced by heating with a gas flame and by using a nonferrous filler metal having a melting point above 800 °F (427 °C), but below that of the base metal. The filler metal is distributed in the joint of capillary attraction.

TOUCH START : A low-voltage, low-amperage arc starting procedure for TIG (GTAW). The tungsten is touched to the workpiece; when the tungsten is lifted from the workpiece an arc is established.

TRANSVERSE SEAM WELDING: The making of a seam weld in a direction essentially at right angles to the throat depth of a seam welding machine.

TUNGSTEN : Rare metallic element with extremely high melting point (3410^o Celsius). Used in manufacturing TIG electrodes.

TUNGSTEN ELECTRODE: A non-filler metal electrode used in arc welding or cutting, made principally of tungsten.

UNDERCUT: A groove melted into the base metal adjacent to the toe or root of a weld and left unfilled by weld metal.

UNDERCUTTING: An undesirable crater at the edge of the weld caused by poor weaving technique or excessive welding speed.

UPSET: A localized increase in volume in the region of a weld, resulting from the application of pressure.

UPSET WELDING: A resistance welding process in which fusion is produced simultaneously over the entire area of abutting surfaces, or progressively along a joint, by the heat obtained from resistance to the flow of electric current through the area of contact of those surfaces. Pressure is applied before heating is started and is maintained throughout the heating period.

UPSETTING FORCE: The force exerted at the welding surfaces in flash or upset welding.

VOLTAGE-SENSING WIRE FEEDER : Feeder operates from arc voltage generated by welding power source.

VOLT-AMP CURVE : Graph that shows the output characteristics of a welding power source. Shows voltage and amperage capabilities of a specific machine.

WANDERING BLOCK SEQUENCE: A block welding sequence in which successive weld blocks are completed at random after several starting blocks have been completed.

WANDERING SEQUENCE: A longitudinal sequence in which the weld bead increments are deposited at random.

WAX PATTERN: Wax molded around the parts to be welded by a thermit welding process to the form desired for the completed weld.

WEAVE BEAD: A type of weld bead made with transverse oscillation.

WEAVING: A technique of depositing weld metal in which the electrode is oscillated. It is usually accomplished by a semicircular motion of the arc to the right and left of the direction of welding. Weaving serves to increase the width of the deposit, decreases overlap, and assists in slag formation.

WELD: A localized fusion of metals produced by heating to suitable temperatures. Pressure and/or filler metal may or may not be used. The filler mkal has a melting point approximately the same or below that of the base mtals, but always above 800 °F (427 °C).

WELD BEAD: A weld deposit resulting from a pass.

WELD GAUGE: A device designed for checking the shape and size of welds.

WELD METAL: That portion of a weld that has been melted during welding.

WELD SYMBOL: A picture used to indicate the desired type of weld.

WELDABILITY: The capacity of a material to form a strong bond of adherence under pressure or when solidifying from a liquid.

WELDER CERTIFICATION: Certification in writing that a welder has produced welds meeting prescribed standards.

WELDER PERFROMANCE QUALIFICATION: The demonstration of a welder's ability to produce welds meeting prescribed standards.

WELDING LEADS: a. Electrode lead. The electrical conductor between the source of the arc welding current and the electrode holder. b. Work lead. The electrical conductor between the source of the arc welding current and the workpiece.

WELDING PRESSURE: The pressure exerted during the welding operation on the parts being welded.

WELDING PROCEDURE: The detailed methods and practices including all joint welding procedures involved in the production of a weldment.

WELDING ROD: Filler metal in wire or rod form, used in gas welding and brazing processes and in those arc welding processes in which the electrode does not provide the filler metal.

WELDING SYMBOL: The assembled symbol consists of the following eight elements, or such of these as are necessary: reference line, arrow, basic weld symbols, dimension and other data, supplementary symbols, finish symbols, tail, specification, process, or other references.

WELDING TECHNIQUE: The details of a manual, machine, or semiautomatic welding operation which, within the limitations of the prescribed joint welding procedure, are controlled by the welder or welding operator.

WELDING TIP: The tip of a gas torch especially adapted to welding.

WELDING TORCH: A device used in gas welding and torch brazing for mixing and controlling the flow of gases.

WELDING TRANSFORMER: A device for providing current of the desired voltage.

WELDMENT: An assembly whose component parts are formed by welding.

WIRE FEED SPEED: Expressed in in/min or mm/s, and refers to the speed and amount of filler metal fed into a weld. Generally speaking the higher the wire feed speed, the higher the amperage.

WORK LEAD: The electric conductor (cable) between the source of arc welding current and the workpiece.

WORKPIECE CONNECTION : A means to fasten the work lead (work cable) to the work (metal to be welded on). Also, the point at which this connection is made. One type of work connection is made with an adjustable clamp.

WORKPIECE LEAD : The conductor cable or electrical conductor between the arc welding machine and the work.

X-RAY: A radiographic test method used to detect internal defects in a weld.

YIELD POINT: The yield point is the load per unit area value at which a marked increase in deformation of the specimen occurs with little or no increase of load; in other words, the yield point is the stress at which a marked increase in strain occurs with little or no increase in stress.